South Texas is contemplating performing zinc injection to reduce crud
and doses. However, as a high duty plant, we are also worried about
kicking off CIPS/AOA. Up to now, we have not had this phenomenon - and
I'd like to stay away from it.
I would like to get the reactor engineers' take on
(1) your opinion on zinc injection v CIPS
(2) if your plant has performed Zn injection,
a. what consideration was given to potential CIPS issues?
b. what has been your experience with the core?
(3) If your plant has decided not to pursue Zn injection, what were
the reasons (was CIPS a factor)?
Thank you for your response.
Duane Gore
Reactor Engineering Supervisor
South Texas Project
(361) 972-8909
degore(a)stpegs.com